EURO POLYMERS UREA-1000H/R - High Grade Polyurea Waterproof Membrane

Origin:  KOREA

Packing: 415 Kg/Set (R: 215Kg, H: 200Kg)

EURO POLYMERS UREA-1000H/R

UREA-1000R/H is a 100% solid content, no-VOC, 2 component Polyurea. Hot spray applied, very fast curing and drying to form a Polyurea waterproofing membrane with wear and impact resistance, high tensile strength properties. The membrane is working well in low temperature, chemical resistance and good adhesion to substrate .

APPLICATION RANGE

•    Waterproofing to concrete, wooden, iron and steel structures for Airport,   apartment, water retaining structure, ...
•     Use for chemical contacting areas
•     Use for oil resistant areas
•     Use as the versatile protection membrane

FFEATURES & BENEFITS

•     No-VOC content
•     Very fast curing time (30 sec.)
•     High tensile strength and highly elastic
•     Withstand in low temperature
•     Resistance to thermal shock
•     Excellent chemical resistance: solvents, oils and acid, ...
•     Excellent adhesion strength to proper prepared surfaces
Note: for sunlight direct contact areas, 2 coats of Euro Polymers UP-266 top coat at 0.25-0.30 kg/m2 are recommended to protect UREA-1000R/H against discolored

SURFACE PREPARATION

The substrate should be dry, clean and free from laitance, oil, dust, paint residues, algae, loose and friable material must be completely removed from all surfaces before application of the product

PRIMING

Use Euro Polymers UP-100 Primer, leave it dry for 1-4 hours prior application of UREA - 1000R/H

CONSUMPTION

•     1.10 kg/ m²/mm (UREA-1000R: 0.55kg, UREA-1000: 0.55kg)

•     The consumption may vary subjected to the substrate condition.

TECHNICAL DATA

Dry time (25°C) 10~30 giây
Shore D hardness 45~50 (D)
Tensile strength (N/mm2) > 16
Elongation at break (%) > 300
Tear strength (N/mm) > 50
Service temperature (°C) 0 ~ 100
Chemical resistance (Soak in 168 hours at room temperature)
10% - Axit Sulforic                                                                                No change
30% - Sodiumcloride                                                                                No change
30% - Sodiumhydroxide                                                                         No change
50% - Sodiumhydroxide                                                                        No change
Diesel                                                                                                     No change
Salt water No change

MATERIAL PROPERTY

Criteria UREA-1000R UREA-1000H
Type Isocyanate Prepolymer Amine Mixture
Form Amber liquid Colored liquid
Viscosity (cps at 25oC) 400~600 400~600
Mixing ratio (by weight) 1 1
Solid content (%) 100 100